1. The heat treatment quality of the aluminum extrusion die directly affects the service life of the extrusion die. The die is hardened by "+" tempering several times to reach the hardness requirements. Quenching is to improve the hardness of the die, and multiple tempering is to improve the toughness of the die and stabilize the internal organization. The hardness value of the die heat treatment is specified as follows: large aluminum extrusion die (F>500 mm), HRC45-48; Srednji kalup (F300~500mm), HRC47-50; Mala kalupa za ekstruziju (F<300mm), hrc48-51;="" test="" three="" points="" on="" the="" same="" plane="" of="" a="" set="" of="" molds,="" and="" the="" hardness="" values="" of="" each="" point="" should="" be="" qualified="" within="" the="" specified="">
2. Posebnu pažnju treba obratiti na sljedeće točke u procesu toplinske obrade ekstruzione matrice:
a. Brzina zagrijavanja visokotemperaturne sekcije treba biti brza, a vrijeme držanja ne smije biti predugo, kako bi se spriječilo pregorevanje ili pregrijavanje kalupa za ekstruziju. Pregrijana -- krupna zrna, pregoreli -- elementi niske tačke topljenja i inkluzija će se rastvoriti;
b. Temperirati aluminijsku matricu za ekstruziju na vrijeme nakon gašenja kako bi se spriječile pukotine;
c. Kada se utvrdi da je tvrdoća matrice za ekstruziju nedovoljna ili neujednačena nakon termičke obrade, treba je žariti, a toplinsku obradu ponoviti prema postupku (kada je vrijednost tvrdoće manja od HRC35, žarenje nije dozvoljeno, a termička obrada se vrši direktno);
d. Za velike aluminijske kalupe za ekstruziju ili gotove kalupe sa složenom šupljinom, treba dodati proces smanjenja naprezanja i kaljenja (da bi se eliminisala električna obrada i naprezanje strojne obrade, odnosno da bi se eliminirao termički stres i organizacijski stres);
e. Da li temperatura ulja za gašenje treba biti? 100 stepeni da bi se osigurao efekat gašenja.