1. The quality of heat treatment of aluminum extrusion die directly affects the service life of the extrusion die. Quenching is to improve the hardness of the mold, and repeated tempering is to improve the toughness of the mold and stabilize the internal structure. The hardness value of mold heat treatment is specified: large aluminum extrusion die (F>500mm), HRC45-48; Srednji kalup (F300 ~ 500mm), HRC47-50; Mali ekstruzija umire (f<300mm), HRC48-51; Three points are tested on the same plane of a set of molds, and the hardness value of each point should be qualified within the specified range.
2. Posebnu pažnju treba posvetiti nekoliko točaka u procesu zagrijavanja u proraču za ekstruziju umrijeti:
a. Brzina grijanja na visokoj temperaturi trebala bi biti brza, a zadržavanje ne bi trebalo biti predugo, kako bi se spriječilo da se ekstruzija umre od pregrijavanja ili pregrijavanja, pregrijavanja - grubo zrna, pregrijavanje - pregrijavanje, pregrijavanje i uključivanja, uzrokovat će raspuštanje;
b. Nakon gašenja, aluminijski ekstruzija umire treba ublažiti na vrijeme kako bi se spriječilo pukotine;
c. Kad se tvrdoća ekstrudiranja utvrdi da je nedovoljna ili neravnomjerna nakon termičke obrade, treba provesti žarenje, a toplotna obrada treba se izvršiti u skladu s postupkom (kada je vrijednost tvrdoće
d. Za velike aluminijske plijesni ili gotovih kalupa sa složenim šupljinama treba dodati, treba dodati temperijski proces ublažavanja (za uklanjanje električne obrade i obrade stresa, odnosno za uklanjanje termičkog stresa i stresa mikrostrukture);
e. Temperatura ublažavanja ulja kalupa trebala bi biti 100 stepeni kako bi se osiguralo efekt gašenja.